Aluminum Balls
Aluminum balls are mainly used in the stud welding industry in place of fasteners for construction, industrial and automotive applications. Our harder Aluminum balls made from 1100-H16 material are used in aircraft and automotive applications where durability and weight are factors. Other tempers of 2017 Aluminum can be supplied, from T0 to T6. Other alloys of Aluminum available upon request. Aluminum balls are corrosion resistant and light in weight. Aluminum balls are available in a range of sizes and tolerances (grades).
| 1100 H16 ALUMINUM BALLS | |||
| 1100 H16 ALUMINUM BALLS are primarily used in the Stud Welding Industry as fasteners. | |||
| SIZE RANGE | 0.50mm (.020") up to 1-1/4" | ||
| GRADES | 200, 500, 1000, 2000 | ||
| CHEMICAL COMPOSTION | |||
| COPPER | .05%-.20% MAX. | ||
| MAGNESIUM | |||
| MANGANESE | .05% MAX. | ||
| SILICON | |||
| IRON | |||
| ZINC | |||
| ALUMINUM | BALANCE | ||
| PHYSICAL CHARACTERISTICS | |||
| EXCELLENT WELDING CAPABILITIES NOT HARDENABLE | |||
| GENERAL USAGE | |||
| STUD WELDING (AUTOMOTIVE, CONSTRUCTION & INDUSTRIAL) | |||
| 2017-T4 ALUMINUM BALLS | |||
| 2017-T4 ALUMINUM BALLS are used in Automotive and Aircraft Applications, where durability, hardness & weight are factors. | |||
| SIZE RANGE | 0.50mm (.020") up to 1-1/4" | ||
| GRADES | 200, 500, 1000, 2000 | ||
| CHEMICAL COMPOSTION | |||
| COPPER | 3.5-4.5% MAX. | ||
| MAGNESIUM | .4%-1.0% MAX. | ||
| MANGANESE | .40%-.80% MAX. | ||
| SILICON | .20%-.80% MAX. | ||
| IRON | .7% MAX. | ||
| ZINC | .25% MAX. | ||
| ALUMINUM | BALANCE | ||
| PHYSICAL CHARACTERISTICS | |||
| HARDNESS | .20-.80 | ||
| GOOD DURABILITY,HARDNESS & WEIGHT | |||
| GENERAL USAGE | |||
| AIRCRAFT APPLICATIONS AUTOMOTIVE APPLICATIONS | |||